| Brand Name: | HAOLISEN |
| Model Number: | HL-1607LB/HLS-1701A |
| Certification: | IATF16949 , ISO9001 |
| Place of Origin: | Shanghai China （Mainland） |
| MOQ: | Negotiation |
| Price: | Negotiation |
| Supply Ability: | 200 Tons Per Day |
| Delivery Time: | 30-60 Days |
| Packaging Details: | 50kg、60 kg、200kg、1000kg packaging barrels |
| Application field: | Car seat |
| Color: | Black |
| main ingredients: | Titanium pigment;carbon black, kaolin |
| Cooperation case: | SAIC Motor |
| Company Info. |
| HLS Coatings （Shanghai）Co.Ltd |
| Verified Supplier |
| View Contact Details |
| Product List |
Solution for the Car seat electrophoresis paint.
Product Introduction
HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
Good stability of bath can adaptable for a longer updating cycle.
Strong anti-corrosion properties,good salt spray resistance workpiece edge.
Main ingredients
Curing agent: Fully enclosed multi isocyanate
Additives: surface active agent, prevent shrinkage cavity agent
Filling tank proportion and method
⑴ Bath preparation
Ratio:
Resin 800.00-1200.00
Paste 200.00
DI water 2000.00
Total 3400.00
⑵ Ripening conditions
Sample quantity: 3000～3400g
Container: 4L (Diameter 16cm)
Tank temperature: 28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)
Storage, packaging and transportation
| This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use. |
Customer production site
|
Two Component E Coating Car Body Painting Grey Color Scratch Resistant
Non - Inflammable Cationic Epoxy Electrocoat , Edpaint For Car Protective Coating
Stone Resistant E Coating Car Body Paint With Anti Rust Pigment Ingredients
High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For Car Wipers
Automotive Hub Epd Coating , Black Cationic Epoxy Cataphoresis Coating
Ultra Low Temperature Electrophoretic Coating Anti Corrosion Coating For Car
Electrolysis E Coating Car Body Painting With Better Substrate Hiding
Car Door Cationic Epoxy Edp Paint , Electrophoretic Lacquer Coating No Stratified State
Flat Appearance E Coating Car Body Paint With Organic Acid / Alcohol Ether Ingredients
Corrosion Resistant Electrodeposition Paint , Pickup Car Body Coating Electrocoat