High Temperature Environments Alloy Steel Seamless Pipes ASTM B674 , STM B619

Categories Alloy Steel Pipe
Brand Name: Torich
Model Number: Alloy Steel Pipe Hastelloy C-4
Certification: CE PED
Place of Origin: China
MOQ: 1000kg
Price: negotiable
Payment Terms: L/C, T/T
Supply Ability: 200 tons per year
Delivery Time: 6-8 weeks
Packaging Details: In bundles in woode box
Application: in most of the chemical industry and high-temperature environments
standard: ASTM B674,STM B619 and so on
grade: W.NR 2.4610 UNS N06455 AWS 052 Alloy C-4
Melting Temperature Range: 1335 ~ 1380 ℃
Material: Hastelloy C-4
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    • Product Details
    • Company Profile

    High Temperature Environments Alloy Steel Seamless Pipes ASTM B674 , STM B619

    Alloy Steel Pipe Hastelloy C-4


    Hastelloy C-4 Application:

    Hastelloy C-4 has been widely used in most of the chemical industry and high-temperature environments.

    Typical fields of application:

    ● flue gas desulfurization system

    ● pickling and acid regeneration plant

    ● production of acetic acid and agrochemicals

    ● production of titanium dioxide (chloride method)

    ● electrolytic plating


    The corrosion resistance of Hastelloy C-4:

    Higher molybdenum and chromium content make Hastelloy C-4 alloy can resist various aggressive chemical media, including reducing media, such as phosphoric acid, hydrochloric acid, sulfuric acid, chlorine, chlorine-containing organic or inorganic media. Due to the high nickel content, Hastelloy C-4 can effectively resist chlorine caused due to stress corrosion cracking, and even hot chloride solution.


    Hastelloy C-4 is characterized by:

    ● In the oxidation and reduction status, for most corrosive medium has excellent corrosion resistance.
    In emulsion has excellent resistance to local corrosion.

    Standard of Hastelloy C-4: ASTM B674,STM B619 and so on


    Hastelloy C-4 grades and standards:

    Grades and StandardsMaterial Gradespecifications
    chemical compositionPipeSheetBarStripWireForging
    SeamlessWelded pipe
    France
    AFNOR
            
    Germany
    DIN
    VdTÜV
    W.Nr.2.4610
    NiMo16Cr16Ti
    17744
    424
    17751 17750
    424
    17752
    424
    17750424 
    United Kingdom
    BS EN
             
    United States
    ASTM
    AME
    UNS NO6455 B622
    SB622
    B619/626
    SB619/626
    B575
    SB575
    B574
    SB574
    B575
    SB575
     B366
    SB366
    ISONiMo16Cr16Ti        

    Hastelloy C-4 chemical composition:

    NiCrFeCMnSiMoTiCoPS
    Margin14.5-17.53.0≤0.009≤1≤0.0514.0-17.0≤0.07≤2.0≤0.02≤0.01

    Hastelloy C-276 Physical properties:

    Density: ρ = 8.6g / cm3

    melting temperature range: 1335 ~ 1380 ℃


    Temperature
    Specific Heat Capacity
    J/( kg · K )
    coefficient of thermal conductivity
    W/mK
    resistivity
    Ω·m
    Elastic Modulus
    KN/mm²
    expansion coefficient
    10-6/K
    0406    
    2040810.1124211 
    93     
    10042611.412520710.9
    20044813.212620211.9
    204     
    3004651512719512.5
    316     
    40047716.712818812.9
    427     
    50049018.412918113.2
    538     
    60050220.513217513.6
    649     
    70051222.613516814
    760     
    80052224.813815814.5
    871     
    900   14915.1
    982     
    1000   13815.9

    Hastelloy C-4 ISO-V notch test:

    Mean ≥120J / cm² at room temperature

    ≥120J / cm² -196 ℃


    Hastelloy C-4 Heating:

    Before the heat treatment and heat treatment process should always be kept clean and pollution-free workpieces.

    During the heat treatment can not touch the sulfur, phosphorus, lead and other low melting point metal, otherwise Nicrofer 6616 hMo alloy becomes brittle, should pay attention to remove paint, such as tags, temperature indicating paint, crayons, oil, fuel and other contaminants. Fuel sulfur content as low as possible, the sulfur content of natural gas should be less than 0.1%, heavy oil should be less than 0.5% sulfur content. Electric heating is a better choice, because precise temperature furnace, furnace gas and clean. If the gas furnace gas furnace clean enough, you can choose from.

    Furnace gas furnace with a neutral to slightly reducing appropriate, should avoid furnace gas fluctuates between oxidation and reduction, heated by the flame is not burning directly to the workpiece.


    Heat treatment:

    1. HastelloyC-4 thermal processing temperature range of 1080 ℃ ~ 950 ℃, cooling method for cooling or rapid air cooling.
    2. To ensure the best corrosion resistance, thermal processing should be carried out after the heat treatment, the workpiece should be directly added to the warmed heat treatment furnaces.


    Hastelloy C-4 Heat Treatment:

    1. Hastelloyc-4 solution treatment temperature range 1050 ℃ ~ 1100 ℃.
    2. The cooling method is water quenching, the material thickness of less than 1.5mm can also be used to quickly cooled.
    3. During the heat treatment, the workpiece must be kept clean.


    Hastelloy C-4 descaling:

    1. Hastelloyc-4 surface oxide and weld around the slag adhesion stronger than stainless steel, is recommended to use fine grain belt or fine grain grinding wheel.
    2. Before using HNO3 / HF mixed acid pickling to blasting or grinding the oxide film break.



    Quality High Temperature Environments Alloy Steel Seamless Pipes ASTM B674 , STM B619 for sale
    Send your message to this supplier
     
    *From:
    *To: TORICH INTERNATIONAL LIMITED
    *Subject:
    *Message:
    Characters Remaining: (0/3000)
     
    Inquiry Cart 0